PTFE Special Compound

Special compounds compliment the series of standard “G” compounds.
Guarniflon® special compounds are gaining more and more market share due to the increasing demand for solution to high tech industrial applications.
The associated table illustrates the properties of some special “G” compounds by Guarniflon®. They represent only a small number of the compounds available among the range of solutions Guarniflon® is able to suggest.
Some of Guarniflon® compounds include fillers like PEEK, PPS, polyimide, LCP, molybdenum disulphide, etc.
 

SPECIAL COMPOUNDS AVAILABLE

In addition to virgin PTFE G400 products, GUARNIFLON® offers a wide range of compounded products as well. Among these compounds, processed directly in Guarniflon® compounding unit starting from selected polymers and special high-purity fillers, end users are enabled to find the right answer to their technical requirements.
To make their selection easier, the following tables resume:

  • the correlation among single fillers, properties and common uses
  • properties of standard and special compounds among those most commonly marketed
The following table shows the way each filler affects physical and mechanical properties.
Combinations of two or more fillers (not considered in the table) allow a large number of compounds. Thus the resulting combined properties offer a variety of applications.
Filler Property Most common applications
Glass Enhanced wear resistance.
Enhanced chemical resistance (except for alkali and hydrofluoric acid).
Valve seats, seals, bearings, requested to resist sliding and chemicals.
Suitable for bearings working at low PV values.
Graphite Extremely low coefficient of friction. Fairly good compressive strength. Good wear resistance. Bearings for high speed on fairly hard surface.
Carbon Good thermal conductivity.
Good resistance to deformation.
Valve seats.
Bearings for high speed and when fast dissipation of electric charges is needed.
Elastic bands for unlubricated compressors.
Molibdenum disulphide Enhanced non-stick properties.
Low static coefficient of friction.
Fairly good resistance to deformation.
Guide bands.
Details needing good resistivity.
Bronze Enhanced compressive strength. Good wear resistance and high thermal conductivity. Anti-extrusion rings.
Unlubricated bearings for high speed on not hard surface.
Guarniflon® can offer an extremely wide range of skived tapes, sheets, extruded and moulded rods and tubes, in virgin PTFE as well as compounded from G series.
Dimensions and relevant tolerances are included in the Dimensional Brochure. Tapes, sheets and finished products can be supplied etched.

MAIN PROPERTIES | MOULDED

Property Test method Unit
G Special Compounds
G416
40% BRONZE
2% CARBON
G418
15% GLASS FIBER
5% MOS2
G420
50% STEEL
G427
40% BRONZE
5% MOS2
G436
3% MOS2
G455
35% CARBOGRAPHITE
G456
25% HARD CARBON
MOULDED
Specific gravity ASTM D792 g/cm3 2.98 - 3.16 2.20 - 2.30 3.25 - 3.35 3.15 - 3.25 2.18 - 2.24 1.90 - 2.00 2.05 - 2.11
Coefficient of linear thermal expansion 25-100 °C ASTM D696 10-5 (mm/mm)/°C 8 - 11 9 - 12 10 - 12 9 - 12 11 - 12 6.5 - 10 8 - 11
Hardness Shore D ASTM D2240 Punti ≥ 58 ≥ 55 ≥ 65 ≥ 60 ≥ 50 ≥ 65 ≥ 62
Tensile strength ISO 527 v=50mm/min N/mm2 ≥ 20 ≥ 18 ≥ 17 ≥ 20 ≥ 23 ≥ 8 ≥ 12
Elongation at break ISO 527 v=50mm/min % ≥ 220 ≥ 230 ≥ 180 ≥ 200 ≥ 230 ≥ 40 ≥ 70
Compressive strength at 1% deformation ASTM D695 N/mm2 8-10 8-9 10 - 10.5 6.5 - 8 5.5 - 6.5 12 - 13.5 7 - 11
Deformation under load (24 h 13.7 N/mm2 23°C ASTM D621 % ≤ 8 ≤ 8 ≤ 6.5 ≤ 7.5 ≤ 14 ≤ 6 ≤ 5.5
Permanent deformation (as above after 24 hdi relaxation) ASTM D621 % ≤ 5 ≤ 4 ≤ 3 ≤ 3.5 ≤ 6 ≤ 1.5 ≤ 1.9
Kinetic coefficient of friction ASTM D1894 / 0.13 0.08 0.13 0.13 0.08 0.12 0.12
Wear factor at PV 100 ASTM D3702 9 - 13 10 - 20 20 - 30 10 - 15 3.000 20 - 30 12 - 18
 

PROPERTIES OF IMPORTANCE FOR DESIGNING

Fillers mixed with PTFE allow to improve some basic physical properties of virgin polymer.
The advantages are the following:

  • enhanced compressive strength
  • enhanced thermal conductivity
  • reduced thermal expansion
  • reduced wear factor
MECHANICAL PROPERTIES
When talking about the material mechanical properties, tensile strength and elongation at break are usually the topics before others.
However, these two properties, though the most common ones, do not always carefully reflect the behavior of the material itself in some applications, while compressive properties are actually the most important ones. We’d highlight compressive strength at a set deformation, deformation under constant load and permanent deformation at a set temperature.

NEWS& EVENTS

Wednesday, 28 February 2024 11:22

SUPPLIER ENGAGEMENT DAY – UK-FEBRUARY 28, 2024

1 day event in UK fully targeted to the Automotive segment, Maceplast UK with the GM Janine Ward and Guarniflon Technical Manager Giacomo Simoni joining the event.

Read more
Monday, 19 February 2024 13:08

Hannover Messe 2024 – Guarniflon will be there

Guarniflon is joining one of the most representative industrial shows in Europe, Hannover Messe, from 22 to 26 of April, taking part at the coolest event gathering more than 300 international companies related to hydrogen and fuel cells applications.

Read more